Instant Grab Adhesive
XCEL IGA is an instant grab MS Polymer adhesive. It was developed for high strength initial bond. It fixes large panels and heavy objects without support or mechanical fixings, and has high tensile strength. It cures without shrinking, resists vibrations and remains flexible. It is available in 2 colours, grey and white.
Technical Information
| Raw material basis: | MS Polymer |
| Consistency: | Non-slump paste |
| Specific gravity: | approx. 1.55 g/ml |
| Skin forming time: | 5 – 10 minutes (at 23ºC; 50% R.H.) |
| Curing rate: | 2-3 mm/24 hr |
| Resistance to flow (ISO 7390): | approx. 0 mm |
| Consumption: | approx. 50 ml/ linear meter (nozzle diameter: 8mm) |
| Application temperature: | Between 5ºC to 40 ºC |
| Properties of the cured product: | (After one week at 23ºC and 50% R.H.) |
| Service temperature: | -40ºC to +90ºC |
| Shore A hardness (ISO 868): | 65 |
| Max. tensile (ISO 37): | 2,50 MPa. |
| Modulus – elongation at 100% – (ISO 37): | 1,70 Mpa. Max. tensile |
| Elongation at break (ISO 37): | > 250 % |
These values may vary depending on environmental factors such as temperature, moisture, and type of substrates. The time until complete curing may be extended at lower temperature, lower humidity or increasing film thickness.
IGA is available in 2 different colours, each tube has a unique “V” Cut Nozzle to control the flow of the product.
 |
IGA – White |
 |
IGA- Grey |
12 tubes per box
106 Boxes per skid
Check out our latest Videos
IGA Soap Dish Demonstration
XCEL IGA is an instant grab MS Polymer adhesive. It was developed for high strength initial bond. It fixes large panels and heavy objects without support or mechanical fixings, and has high tensile strength. It [...]
IGA Underwater Demonstration
XCEL IGA is an instant grab MS Polymer adhesive. It was developed for high strength initial bond. It fixes large panels and heavy objects without support or mechanical fixings, and has high tensile strength. It [...]
IGA Ladder Demonstration
XCEL IGA is an instant grab MS Polymer adhesive. It was developed for high strength initial bond. It fixes large panels and heavy objects without support or mechanical fixings, and has high tensile strength. It [...]
IGA Materials Demonstration
XCEL IGA is an instant grab MS Polymer adhesive. It was developed for high strength initial bond. It fixes large panels and heavy objects without support or mechanical fixings, and has high tensile strength. It [...]
IGA Weight Demonstration
Xcel IGA is an instant grab MS Polymer adhesive. It was developed for high strength initial bond. It fixes large panels and heavy objects without support or mechanical fixings, and has high tensile strength. It [...]