Masonry Grab Adhesive
XCEL MGA is a very high strength, high viscosity, one-part elastic adhesive for indoor and outdoor applications based on MS Polymer. Specially designed for fast and non-rigid structural bonding in construction, metal industry and masonry sector, with excellent adhesion to most substrates including brick, concrete, ceramics, marble, wood, melamine, aluminium and metals, and most plastics. Completely neutral and odourless curing.
Technical Information
Raw material basis: | MS Polymer |
Consistency: | Non-slump paste |
Specific gravity: | approx. 1.55 g/ml |
Skin forming time: | 15 – 20 minutes (at 23ºC; 50% R.H.) |
Curing rate: | 2-3 mm/24 hr |
Resistance to flow (ISO 7390): | approx. 0 mm |
Consumption: | approx. 50 ml/ linear meter (nozzle diameter: 8mm) |
Application temperature: | Between 5ºC to 40 ºC |
Properties of the cured product: | (After one week at 23ºC and 50% R.H.) |
Service temperature: | -40ºC to +90ºC |
Shore A hardness (ISO 868): | 65 |
Max. tensile (ISO 37): | 2,50 MPa. |
Elongation at break (ISO 37): | > 250 % |
These values may vary depending on environmental factors such as temperature, moisture, and type of substrates. The time until complete curing may be extended at lower temperature, lower humidity or increasing film thickness.
Check out our latest Videos
MGA Cultured Stone Demonstration
XCEL MGA is an instant grab MS Polymer adhesive, specifically developed to bond natural and manufactured stone to a secure substrate. With high strength initial bond, it fixes veneer stones and panels without support or [...]